Characteristics for grade 10KH15N35V3TYU ( 10Х15Н35В3ТЮ )

Grade :	10KH15N35V3TYU ( 10Х15Н35В3ТЮ )
Classification :	Hidh-temperature or heat-resistant alloy
Equivalent grades:	Is absent

Chemical composition in % for grade 10KH15N35V3TYU ( 10Х15Н35В3ТЮ )

Fe	C	Si	Mn	Ni	S	P	Cr	W	Ti	Al	B
36.83 - 45.6	max 0.1	max 0.5	1 - 2	34 - 38	max 0.03	max 0.03	14 - 16	3 - 4	0.7 - 1	1.7 - 1.5	max 0.01

Mechanical properties under Т=20^oС for grade 10KH15N35V3TYU ( 10Х15Н35В3ТЮ )

Assortment	Dimension	Direct.	s_в	s_T	d₅	y	KCU	Heat treatment
-	mm	-	MPa	MPa	%	%	kJ / m²	-
Bars	70	longitudinal	670	430	28	49	1200

Brinell hardness for 10KH15N35V3TYU ( 10Х15Н35В3ТЮ ) ,

HB 10^-1 = 217 MPa

Physical properties for grade 10KH15N35V3TYU ( 10Х15Н35В3ТЮ )

T	E 10^{- 5}	a 10⁶	l	r	C	R 10⁹
Grade	MPa	1/Grade	Watt/(m·Grade)	kg/m³	J/(kg·Grade)	Ohm·m
20	2.02			8160
100	1.99	13.8	13.4
200	1.94	14.1	16.7
300	1.9	15.1	19.4
400	1.83	15.2	22.6
500	1.77	15.7	25.5
600	1.69	16.2	28.5
700	1.61	16.5
800	1.53
T	E 10^{- 5}	a 10⁶	l	r	C	R 10⁹

Specification :

Mechanical properties :
s_в	- Tensile strength , [MPa]
s_T	- Yield stress, [MPa]
d₅	- Specific elongation at fracture , [ % ]
y	- Reduction of area , [ % ]
KCU	- Impact strength , [ kJ / m²]
HB	- Brinell hardness , [MPa]

Physical properties :
T	- Test temperature , [Grade]
E	- Young modulus , [MPa]
a	- Coefficient of linear expansion (range 20^o - T ) , [1/Grade]
l	- Termal (heat) condition coefficient , [Watt/(m·Grade)]
r	- Density , [kg/m³]
C	- Specific heat ( range 20^o - T ), [J/(kg·Grade)]
R	- Electrical resistance , [Ohm·m]

10KH15N35V3TYU ( 10Х15Н35В3ТЮ ) - Hidh-temperature or heat-resistant alloy: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

© 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.