| Grade : | 30 ( 30 ) |
| Substitute: | 25, 35 |
| Classification : | High quality structural carbon steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 30 ( 30 )
| C | Si | Mn | Ni | S | P | Cr | Cu | As |
| 0.27 - 0.35 | 0.17 - 0.37 | 0.5 - 0.8 | max 0.3 | max 0.04 | max 0.035 | max 0.25 | max 0.3 | max 0.08 |
Temperature of critical points for grade 30 ( 30 ).
| Ac1 = 730 , Ac3(Acm) = 820 , Ar3(Arcm) = 796 , Ar1 = 680 , Mn = 380 |
Mechanical properties under Т=20oС for grade 30 ( 30 )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Sheet heat-treatment, GOST 4041-71 | 4 - 14 | 430-590 | 24 | |||||
| Rolled stock, GOST 1050-88 | to 80 | 490 | 295 | 21 | 50 | Normalizing | ||
| Rolled stock cold-worked , GOST 1050-88 | 560 | 7 | 35 | |||||
| Rolled stock annealed , GOST 1050-88 | 440 | 17 | 45 | |||||
| Band annealed , GOST 2284-79 | 390-640 | 16 | ||||||
| Band cold-worked , GOST 2284-79 | 640-930 |
| Brinell hardness for 30 ( 30 ) , Sheet GOST 4041-71 | HB 10 -1 = 149 MPa |
| Brinell hardness for 30 ( 30 ) , Rolled stock GOST 1050-88 | HB 10 -1 = 229 MPa |
| Brinell hardness for 30 ( 30 ) , Rolled stock GOST 1050-88 | HB 10 -1 = 179 MPa |
| Brinell hardness for 30 ( 30 ) , Rolled stock GOST 1050-88 | HB 10 -1 = 179 MPa |
Technological properties for grade 30 ( 30 )
| Weldability: | limited weldability. |
| Flakes : | not predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade 30 ( 30 )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2 | 52 | 7850 | |||
| 100 | 1.96 | 12.1 | 51 | 470 | ||
| 200 | 1.91 | 12.9 | 49 | 483 | ||
| 300 | 1.85 | 13.6 | 46 | 546 | ||
| 400 | 14.2 | 43 | 563 | |||
| 500 | 14.7 | 39 | 764 | |||
| 600 | 1.64 | 15 | 36 | |||
| 700 | 15.2 | 32 | ||||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 30 ( 30 )
| USA | Germany | Japan | France | England | European | Italy | China | Bulgaria | Poland | Romania | Czechia | ||||||||||||||||||||||||||||||||
| - | DIN,WNr | JIS | AFNOR | BS | EN | UNI | GB | BDS | PN | STAS | CSN | ||||||||||||||||||||||||||||||||
|
|
|
|
|
|
|
|
|
|
|
|
Types of delivery of grade 30 ( 30 )
| B03 - Metal forming treatment. Forgings |
| В05 - Welding and cutting of metals., Soldering, riveting |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| B24 - Ribbons |
| В32 - Graded and shaped rolling |
| B33 - Sheets and Strips |
| B34 - Ribbons |
| В62 - Steel pipes and connecting parts to them |
| В71 - Low-carbon steel wire |
| В72 - Medium-high and high-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
30 ( 30 ) - High quality structural carbon steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |