Characteristics for grade 11KH11N2V2MF ( 11Х11Н2В2МФ )

Grade :	11KH11N2V2MF ( 11Х11Н2В2МФ ) ( Х12Н2ВМФ ЭИ962 )
Classification :	High alloy high-temperature steel
Equivalent grades:	Is absent

Chemical composition in % for grade 11KH11N2V2MF ( 11Х11Н2В2МФ )

C	Si	Mn	Ni	S	P	Cr	Mo	W	V
0.09 - 0.13	max 0.6	max 0.6	1.5 - 1.8	max 0.025	max 0.03	10.5 - 12	0.35 - 0.5	1.6 - 2	0.18 - 0.3

Mechanical properties under Т=20^oС for grade 11KH11N2V2MF ( 11Х11Н2В2МФ )

Assortment	Dimension	Direct.	s_в	s_T	d₅	y	KCU	Heat treatment
-	mm	-	MPa	MPa	%	%	kJ / m²	-
Bar, GOST 5949-75			835-980	735-835	10-12	50-55	590-690
Sheet thin, GOST 5582-75			830		22			Annealing 760 - 780^oC,

Brinell hardness for 11KH11N2V2MF ( 11Х11Н2В2МФ ) (annealing) , Bar GOST 5949-75

HB 10^-1 = 285 MPa

Types of delivery of grade 11KH11N2V2MF ( 11Х11Н2В2МФ )

В22 - Graded and shaped rolling

B23 - Sheets and Strips

В32 - Graded and shaped rolling

B33 - Sheets and Strips

Specification :

Mechanical properties :
s_в	- Tensile strength , [MPa]
s_T	- Yield stress, [MPa]
d₅	- Specific elongation at fracture , [ % ]
y	- Reduction of area , [ % ]
KCU	- Impact strength , [ kJ / m²]
HB	- Brinell hardness , [MPa]

Physical properties :
T	- Test temperature , [Grade]
E	- Young modulus , [MPa]
a	- Coefficient of linear expansion (range 20^o - T ) , [1/Grade]
l	- Termal (heat) condition coefficient , [Watt/(m·Grade)]
r	- Density , [kg/m³]
C	- Specific heat ( range 20^o - T ), [J/(kg·Grade)]
R	- Electrical resistance , [Ohm·m]

11KH11N2V2MF ( 11Х11Н2В2МФ ) - High alloy high-temperature steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

© 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.