Characteristics for grade 10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )

Grade :	10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )
Classification :	Casting alloy steel with specific properties
Equivalent grades:	Is absent

Chemical composition in % for grade 10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )

C	Si	Mn	Ni	S	P	Cr	Cu
max 0.1	max 0.6	2.3 - 3	3 - 3.5	max 0.03	max 0.03	13 - 19	1.8 - 2.2

Mechanical properties under Т=20^oС for grade 10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )

Assortment	Dimension	Direct.	s_в	s_T	d₅	y	KCU	Heat treatment
-	mm	-	MPa	MPa	%	%	kJ / m²	-
Casting, GOST 977-88			687	491	12	25	294	Normalizing and drawing

Technological properties for grade 10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )

Weldability:

limited weldability.

Types of delivery of grade 10KH18N3G3D2L ( 10Х18Н3Г3Д2Л )

B82 - Steel Castings

Specification :

Mechanical properties :
s_в	- Tensile strength , [MPa]
s_T	- Yield stress, [MPa]
d₅	- Specific elongation at fracture , [ % ]
y	- Reduction of area , [ % ]
KCU	- Impact strength , [ kJ / m²]
HB	- Brinell hardness , [MPa]

Physical properties :
T	- Test temperature , [Grade]
E	- Young modulus , [MPa]
a	- Coefficient of linear expansion (range 20^o - T ) , [1/Grade]
l	- Termal (heat) condition coefficient , [Watt/(m·Grade)]
r	- Density , [kg/m³]
C	- Specific heat ( range 20^o - T ), [J/(kg·Grade)]
R	- Electrical resistance , [Ohm·m]

Weldability :
without limitations	- welding is done without heating and subsequent heat treeting
limited weldability	- welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability	- obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing

10KH18N3G3D2L ( 10Х18Н3Г3Д2Л ) - Casting alloy steel with specific properties: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

© 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.