Characteristics for grade     09KH17N3SL   ( 09Х17Н3СЛ )



      Grade :     09KH17N3SL   ( 09Х17Н3СЛ )
      Classification :   Casting alloy steel with specific properties
      Equivalent grades:     Is absent



Chemical composition in % for grade   09KH17N3SL   ( 09Х17Н3СЛ )
C Si Mn Ni S P Cr
0.05 - 0.120.8 - 1.50.3 - 0.82.8 - 3.8max   0.03max   0.03515 - 18


Mechanical properties under Т=20oС for grade   09KH17N3SL   ( 09Х17Н3СЛ )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Casting, GOST 977-88     981 736 8 15196Annealing 660 - 670oC,Guenching 1040 - 1060oC,Drawing 300 - 350oC, oil, Cooling air,


Heat treatment of the material   09KH17N3SL   ( 09Х17Н3СЛ )
Annealing 660 - 670 ° C, Hardening 1040 - 1060 ° C, Oil cooling, Tempering 300 - 350 ° C , Air cooling;
Hardening 1040 - 1060 ° C, Oil cooling, Tempering 540 - 560 ° C , Air cooling;
Tempering 670 - 690 ° C , Air cooling;



Types of delivery of grade   09KH17N3SL   ( 09Х17Н3СЛ )
B82 - Steel Castings


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  09KH17N3SL   ( 09Х17Н3СЛ ) - Casting alloy steel with specific properties: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru