| Grade : | 30KhMА ( 30ХМА ) |
| Classification : | Relaxation-resistant steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 30KhMА ( 30ХМА )
| C | Si | Mn | Ni | S | P | Cr | Mo | Cu |
| 0.26 - 0.33 | 0.17 - 0.37 | 0.4 - 0.7 | max 0.3 | max 0.025 | max 0.025 | 0.8 - 1.1 | 0.15 - 0.25 | max 0.3 |
Temperature of critical points for grade 30KhMА ( 30ХМА ).
| Ac1 = 757 , Ac3(Acm) = 807 |
Mechanical properties under Т=20oС for grade 30KhMА ( 30ХМА )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Pipe, GOST 8731-87 | 588 | 392 | 13 | |||||
| Bar, GOST 4543-71 | Ø 15 | 930 | 735 | 12 | 50 | 880 | Guenching 880oC, oil, Drawing 540oC, water, |
| Brinell hardness for 30KhMА ( 30ХМА ) (annealing) , GOST 4543-71 | HB 10 -1 = 229 MPa |
| Brinell hardness for 30KhMА ( 30ХМА ) , Bar GOST 10702-78 | HB 10 -1 = 217 MPa |
Technological properties for grade 30KhMА ( 30ХМА )
| Weldability: | limited weldability. |
| Flakes : | predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade 30KhMА ( 30ХМА )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.08 | 7820 | 230 | |||
| 100 | 2.07 | 11.6 | 46 | 7800 | 462 | |
| 200 | 2.04 | 12.5 | 44 | 7770 | ||
| 300 | 1.97 | 13.2 | 42 | 7740 | ||
| 400 | 1.88 | 13.8 | 42 | 7700 | ||
| 500 | 1.76 | 14.3 | 39 | 7660 | ||
| 600 | 1.6 | 37 | ||||
| 700 | 36 | |||||
| 800 | 32 | |||||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 30KhMА ( 30ХМА )
| USA | Germany | Japan | France | England | European | Italy | Sweden | Austria | |||||||||||||||||||||||||||||||||||
| - | DIN,WNr | JIS | AFNOR | BS | EN | UNI | SS | ONORM | |||||||||||||||||||||||||||||||||||
|
|
|
|
|
|
|
|
|
Types of delivery of grade 30KhMА ( 30ХМА )
| B03 - Metal forming treatment. Forgings |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| В62 - Steel pipes and connecting parts to them |
| В71 - Low-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
30KhMА ( 30ХМА ) - Relaxation-resistant steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |