Characteristics for grade     VZhL12U   ( ВЖЛ12У )



      Grade :   VZhL12U   ( ВЖЛ12У ) (   ВЖЛ12У-ВИ   )
      Classification :   High-temperature casting alloy
      Equivalent grades:     Is absent



Chemical composition in % for grade   VZhL12U   ( ВЖЛ12У )
Fe C Si Mn Ni S P Cr Ce Mo W V Co Nb TiAl Zr B PbBi -
max   20.14 - 0.2max   0.4max   0.453.8 - 63.46max   0.015max   0.0158.5 - 10.5max   0.022.7 - 3.41 - 1.80.5 - 112 - 150.5 - 14.2 - 4.75 - 5.7max   0.02max   0.015max   0.001max   0.0005 Ni - basis
Comment: Ni is a basis; the percentage of Ni is given approximately.


Mechanical properties under Т=20oС for grade   VZhL12U   ( ВЖЛ12У )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Blank     830   5 7  


Material long term strength     VZhL12U   ( ВЖЛ12У )
OCT 1 90126-85
Test temperature   975 ° С
Acting stress   200   MPa
Time to fracture, hours   40



Types of delivery of grade   VZhL12U   ( ВЖЛ12У )
В32 - Graded and shaped rolling


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  VZhL12U   ( ВЖЛ12У ) - High-temperature casting alloy: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru