| Grade : | 55S2 ( 55С2 ) |
| Substitute: | 50С2, 60С2, 35Х2АФ |
| Classification : | Spring structural steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 55S2 ( 55С2 )
| C | Si | Mn | Ni | S | P | Cr | Cu |
| 0.52 - 0.6 | 1.5 - 2 | 0.6 - 0.9 | max 0.25 | max 0.035 | max 0.035 | max 0.3 | max 0.2 |
Temperature of critical points for grade 55S2 ( 55С2 ).
| Ac1 = 755 , Ac3(Acm) = 810 , Ar3(Arcm) = 770 , Ar1 = 690 , Mn = 272 |
Mechanical properties under Т=20oС for grade 55S2 ( 55С2 )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| 760 | 440 | 21 | 42 | 160 | Annealing 750 - 780oC,Cooling oven, | |||
| Rolled stock, GOST 14959-79 | 1270 | 1175 | 6 | 30 | Guenching and drawing |
| Brinell hardness for 55S2 ( 55С2 ) (without heat treatment) , GOST 14959 | HB 10 -1 = 285 MPa |
| Brinell hardness for 55S2 ( 55С2 ) (heat treatment) , Rolled stock GOST 14959-79 | HB 10 -1 = 241 MPa |
Technological properties for grade 55S2 ( 55С2 )
| Weldability: | is not used. |
| Flakes : | not predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade 55S2 ( 55С2 )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 1.96 |
Equivalent steels for grade 55S2 ( 55С2 )
| USA | Germany | Japan | France | England | European | Italy | Belgium | Spain | China | Sweden | Bulgaria | Hungary | Poland | Romania | Australia | ||||||||||||||||||||||||||||
| - | DIN,WNr | JIS | AFNOR | BS | EN | UNI | NBN | UNE | GB | SS | BDS | MSZ | PN | STAS | AS | ||||||||||||||||||||||||||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Types of delivery of grade 55S2 ( 55С2 )
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| B33 - Sheets and Strips |
| В72 - Medium-high and high-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
55S2 ( 55С2 ) - Spring structural steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |