Characteristics for grade 30KHGSFL ( 30ХГСФЛ )

Grade :	30KHGSFL ( 30ХГСФЛ )
Substitute:	35ХНЛ
Classification :	Casting alloy steel for general purposes
Equivalent grades:	Go here

Chemical composition in % for grade 30KHGSFL ( 30ХГСФЛ )

C	Si	Mn	S	P	Cr	V
0.25 - 0.35	0.4 - 0.6	1 - 1.5	max 0.05	max 0.05	0.3 - 0.5	0.06 - 0.12

Mechanical properties under Т=20^oС for grade 30KHGSFL ( 30ХГСФЛ )

Assortment	Dimension	Direct.	s_в	s_T	d₅	y	KCU	Heat treatment
-	mm	-	MPa	MPa	%	%	kJ / m²	-
Casting, GOST 977-88	to 100		589	392	15	25	343	Normalizing 900 - 930^oC,Drawing 600 - 650^oC,
Casting, GOST 977-88			785	589	14	25	441

Heat treatment of the material 30KHGSFL ( 30ХГСФЛ )

Normalizing 900 - 930 ° C, Tempering 600 - 650 ° C

Hardening 900 - 920 ° C, Tempering 630 - 670 ° C

Equivalent steels for grade 30KHGSFL ( 30ХГСФЛ )Warning! Indicated both exact and nearest equivalents.

Japan

Czechia

JIS

CSN

SCMnCr2

422724

Types of delivery of grade 30KHGSFL ( 30ХГСФЛ )

B82 - Steel Castings

Specification :

Mechanical properties :
s_в	- Tensile strength , [MPa]
s_T	- Yield stress, [MPa]
d₅	- Specific elongation at fracture , [ % ]
y	- Reduction of area , [ % ]
KCU	- Impact strength , [ kJ / m²]
HB	- Brinell hardness , [MPa]

Physical properties :
T	- Test temperature , [Grade]
E	- Young modulus , [MPa]
a	- Coefficient of linear expansion (range 20^o - T ) , [1/Grade]
l	- Termal (heat) condition coefficient , [Watt/(m·Grade)]
r	- Density , [kg/m³]
C	- Specific heat ( range 20^o - T ), [J/(kg·Grade)]
R	- Electrical resistance , [Ohm·m]

30KHGSFL ( 30ХГСФЛ ) - Casting alloy steel for general purposes: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

© 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.