| Grade : | 35KHN1M2FА ( 35ХН1М2ФА ) |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Is absent |
Chemical composition in % for grade 35KHN1M2FА ( 35ХН1М2ФА )
| C | Si | Mn | Ni | S | P | Cr | Mo | V | Cu |
| 0.32 - 0.4 | max 0.37 | 0.5 - 0.8 | 1.3 - 1.7 | max 0.022 | max 0.025 | 1.3 - 1.7 | 0.4 - 0.6 | 0.1 - 0.2 | max 0.25 |
Temperature of critical points for grade 35KHN1M2FА ( 35ХН1М2ФА ).
| Ac1 = 750 , Ac3(Acm) = 820 , Mn = 300 |
Mechanical properties under Т=20oС for grade 35KHN1M2FА ( 35ХН1М2ФА )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Forging | 500 - 800 | 785 | 640 | 10 | 30 | 390 | Guenching and drawing |
| Brinell hardness for 35KHN1M2FА ( 35ХН1М2ФА ) (quenching, tempering) , | HB 10 -1 = 248 - 293 MPa |
Technological properties for grade 35KHN1M2FА ( 35ХН1М2ФА )
| Weldability: | is not used. |
| Flakes : | predisposed |
| Temper brittleness: | weakly predisposed |
Types of delivery of grade 35KHN1M2FА ( 35ХН1М2ФА )
| B03 - Metal forming treatment. Forgings |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
35KHN1M2FА ( 35ХН1М2ФА ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |