| Grade : | 20KHN2M ( 20ХН2М ) ( 20ХНМ ) |
| Substitute: | 20ХГР, 15ХР, 20ХНР, 20ХГНР |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 20KHN2M ( 20ХН2М )
| C | Si | Mn | Ni | S | P | Cr | Mo | Cu |
| 0.15 - 0.22 | 0.17 - 0.37 | 0.4 - 0.7 | 1.6 - 2 | max 0.035 | max 0.035 | 0.4 - 0.6 | 0.2 - 0.3 | max 0.3 |
Temperature of critical points for grade 20KHN2M ( 20ХН2М ).
| Ac1 = 720 , Ac3(Acm) = 825 |
Mechanical properties under Т=20oС for grade 20KHN2M ( 20ХН2М )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Bar, GOST 4543-71 | Ø 15 | 880 | 685 | 11 | 50 | 780 | Guenching and drawing |
| Brinell hardness for 20KHN2M ( 20ХН2М ) , Rolled stock GOST 4543-71 | HB 10 -1 = -1 MPa |
Technological properties for grade 20KHN2M ( 20ХН2М )
| Weldability: | limited weldability. |
| Flakes : | predisposed |
| Temper brittleness: | not predisposed |
Equivalent steels for grade 20KHN2M ( 20ХН2М )
| USA | Germany | Japan | ||||||||
| - | DIN,WNr | JIS | ||||||||
|
|
|
Types of delivery of grade 20KHN2M ( 20ХН2М )
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
20KHN2M ( 20ХН2М ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |