| Grade : | 15KHF ( 15ХФ ) |
| Substitute: | 20ХФ |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 15KHF ( 15ХФ )
| C | Si | Mn | Ni | S | P | Cr | V | Cu |
| 0.12 - 0.18 | 0.17 - 0.37 | 0.4 - 0.7 | max 0.3 | max 0.035 | max 0.035 | 0.8 - 1.1 | 0.06 - 0.12 | max 0.3 |
Temperature of critical points for grade 15KHF ( 15ХФ ).
| Ac1 = 741 , Ac3(Acm) = 843 , Ar3(Arcm) = 788 , Ar1 = 704 , Mn = 435 |
Mechanical properties under Т=20oС for grade 15KHF ( 15ХФ )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Bar, GOST 4543-71 | Ø 15 | 740 | 540 | 13 | 50 | 780 | As-delivered state |
| Brinell hardness for 15KHF ( 15ХФ ) (annealing) , GOST 4543-71 | HB 10 -1 = 187 MPa |
| Brinell hardness for 15KHF ( 15ХФ ) (cold-worked) , GOST 4543-71 | HB 10 -1 = 217 MPa |
| Brinell hardness for 15KHF ( 15ХФ ) , Bar GOST 10702-78 | HB 10 -1 = 163 MPa |
Technological properties for grade 15KHF ( 15ХФ )
| Weldability: | without limitations. |
| Flakes : | weakly predisposed |
| Temper brittleness: | weakly predisposed |
Physical properties for grade 15KHF ( 15ХФ )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.06 | 7760 | ||||
| 100 | 11.9 | 43 | 7730 | 281 | ||
| 200 | 12.4 | 42 | 7710 | 345 | ||
| 300 | 13.1 | 42 | 7670 | 421 | ||
| 400 | 13.7 | 40 | 7640 | 513 | ||
| 500 | 14.2 | 36 | 7600 | 606 | ||
| 600 | 14.5 | 34 | 7570 | 731 | ||
| 700 | 14.9 | 30 | 7530 | 833 | ||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 15KHF ( 15ХФ )
| USA | Czechia | |||
| - | CSN | |||
|
|
Types of delivery of grade 15KHF ( 15ХФ )
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| В71 - Low-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
15KHF ( 15ХФ ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |