| Grade : | 35G2 ( 35Г2 ) |
| Substitute: | 40Х |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 35G2 ( 35Г2 )
| C | Si | Mn | Ni | S | P | Cr | Cu |
| 0.31 - 0.39 | 0.17 - 0.37 | 1.4 - 1.8 | max 0.3 | max 0.035 | max 0.035 | max 0.3 | max 0.3 |
Temperature of critical points for grade 35G2 ( 35Г2 ).
| Ac1 = 718 , Ac3(Acm) = 804 , Ar3(Arcm) = 727 , Ar1 = 677 , Mn = 340 |
Mechanical properties under Т=20oС for grade 35G2 ( 35Г2 )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Bar, GOST 4543-71 | Ø 25 | 620 | 365 | 13 | 40 | Guenching 870oC, oil, Drawing 650oC, air, | ||
| Forging | 100 - 300 | 530 | 275 | 17 | 38 | 340 | Normalizing |
| Brinell hardness for 35G2 ( 35Г2 ) (annealing) , GOST 4543-71 | HB 10 -1 = 207 MPa |
Technological properties for grade 35G2 ( 35Г2 )
| Flakes : | predisposed |
| Temper brittleness: | predisposed |
Physical properties for grade 35G2 ( 35Г2 )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.04 | 7790 | ||||
| 100 | 40 | |||||
| 200 | 38 | |||||
| 300 | 37 | |||||
| 400 | 36 | |||||
| 500 | 35 | |||||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 35G2 ( 35Г2 )
| USA | Germany | Japan | France | England | Spain | China | Sweden | Bulgaria | Hungary | Romania | Czechia | South Korea | |||||||||||||||||||||||||||||||||||||||||||
| - | DIN,WNr | JIS | AFNOR | BS | UNE | GB | SS | BDS | MSZ | STAS | CSN | KS | |||||||||||||||||||||||||||||||||||||||||||
|
|
|
|
|
|
|
|
|
|
|
|
|
Types of delivery of grade 35G2 ( 35Г2 )
| B03 - Metal forming treatment. Forgings |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| B33 - Sheets and Strips |
| В71 - Low-carbon steel wire |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
35G2 ( 35Г2 ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys