| Grade : | 10G2 ( 10Г2 ) |
| Substitute: | 09Г2 |
| Classification : | Alloy structurall steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade 10G2 ( 10Г2 )
| C | Si | Mn | Ni | S | P | Cr | Cu |
| 0.07 - 0.15 | 0.17 - 0.37 | 1.2 - 1.6 | max 0.3 | max 0.035 | max 0.035 | max 0.3 | max 0.3 |
Temperature of critical points for grade 10G2 ( 10Г2 ).
| Ac1 = 720 , Ac3(Acm) = 830 , Ar3(Arcm) = 710 , Ar1 = 620 |
Mechanical properties under Т=20oС for grade 10G2 ( 10Г2 )
| Assortment | Dimension | Direct. | sв | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Pipe hot strain, GOST 550-75 | 421 | 265 | 21 | 50 | 1180 | |||
| Pipe, GOST 8731-87 | 421 | 265 | 21 | |||||
| Bar, GOST 4543-71 | Ø 25 | 420 | 245 | 22 | 50 | Guenching | ||
| Sheet trick, GOST 1577-93 | 400 | 29 | Annealing | |||||
| Sheet trick, GOST 1577-93 | 440 | 28 | Normalizing |
| Brinell hardness for 10G2 ( 10Г2 ) (annealing) , GOST 4543-71 | HB 10 -1 = 197 MPa |
| Brinell hardness for 10G2 ( 10Г2 ) , Pipe GOST 550-75 | HB 10 -1 = 197 MPa |
Technological properties for grade 10G2 ( 10Г2 )
| Weldability: | without limitations. |
| Flakes : | not predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade 10G2 ( 10Г2 )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.04 | 7790 | ||||
| 100 | 11.3 | |||||
| 200 | 38 | |||||
| 300 | 37 | |||||
| 400 | 14.7 | 36 | ||||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade 10G2 ( 10Г2 )
| USA | England | ||
| - | BS | ||
|
|
Types of delivery of grade 10G2 ( 10Г2 )
| B03 - Metal forming treatment. Forgings |
| В22 - Graded and shaped rolling |
| B23 - Sheets and Strips |
| В32 - Graded and shaped rolling |
| B33 - Sheets and Strips |
| В62 - Steel pipes and connecting parts to them |
Specification :
| Mechanical properties : | |
| sв | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
10G2 ( 10Г2 ) - Alloy structurall steel: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys
| © 2003 - 2024 Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use. |