Characteristics for grade     BrO10   ( БрО10 )



      Grade :     BrO10   ( БрО10 )
      Classification :   Tin foundry bronzes
      Equivalent grades:     Is absent

Comment: Cu is a basis; the percentage of Cu is given approximately.


Mechanical properties under Т=20oС for grade   BrO10   ( БрО10 )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
cast in a metal mould     295   3-10   
sand (mould) casting     215 175 3-10   


    Brinell hardness for     BrO10   ( БрО10 )   ,     cast in a metal mould HB 10 -1 = 108   MPa
    Brinell hardness for     BrO10   ( БрО10 )   ,     sand (mould) casting HB 10 -1 = 68 - 78   MPa


Friction coefficient of the material   BrO10   ( БрО10 ) .
 Friction coefficient with oil : 0.0056
 Friction coefficient without oil : 0.17


Technological properties of the material   BrO10   ( БрО10 ) .
        Melting temperature : 1020   °C


Physical properties for grade   BrO10   ( БрО10 )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 1.04 18.5 48.1 8800 368.4  




Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  BrO10   ( БрО10 ) - Tin foundry bronzes: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru