YOU HERE:   Steel and Alloy   ->   Latten (copper-zinc alloy)

Characteristics for grade     LTS40SD   ( ЛЦ40СД )



      Grade :   LTS40SD   ( ЛЦ40СД ) (   ЛС59-1ЛД   )
      Classification :   Cast cooper-zinc alloys
      Equivalent grades:     Is absent



Chemical composition in % for grade   LTS40SD   ( ЛЦ40СД )
Fe Si Mn NiAl Cu PbZn Sb Sn Impurity
max   0.5max   0.2max   0.2max   1max   0.258 - 610.8 - 235.5 - 41.2max   0.05max   0.3 all 1.5
Comment: Zn is a basis; the percentage of Zn is given approximately.


Mechanical properties under Т=20oС for grade   LTS40SD   ( ЛЦ40СД )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
cast in a metal mould, GOST 17711-93     264   18    
die casting, GOST 17711-93     196   6    


    Brinell hardness for     LTS40SD   ( ЛЦ40СД )   ,     cast in a metal mould GOST 17711-93 HB 10 -1 = 100   MPa
    Brinell hardness for     LTS40SD   ( ЛЦ40СД )   ,     die casting GOST 17711-93 HB 10 -1 = 70   MPa



Types of delivery of grade   LTS40SD   ( ЛЦ40СД )
B51 - Non-ferrous metals, including rare metals, and their alloys


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  LTS40SD   ( ЛЦ40СД ) - Cast cooper-zinc alloys: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys

    ©   2003 - 2024         Database of Steel and Alloy (russian title is the Marochnik)
Administration of the Marochnik is not responsible for the content's use.
Рейтинг@Mail.ru