Characteristics for grade     LАZH60-1-1   ( ЛАЖ60-1-1 )



      Grade :     LАZH60-1-1   ( ЛАЖ60-1-1 )
      Classification :   Copper-zinc alloys pressure treated
      Equivalent grades:   Go here



Chemical composition in % for grade   LАZH60-1-1   ( ЛАЖ60-1-1 )
FeMn PAl Cu PbZn Sb Bi Impurity
0.75 - 1.50.1 - 0.6max   0.010.7 - 1.558 - 61max   0.434.7 - 40.4max   0.005max   0.002 all 0.7
Comment: Zn is a basis; the percentage of Zn is given approximately.


Mechanical properties under Т=20oС for grade   LАZH60-1-1   ( ЛАЖ60-1-1 )
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Bar, GOST 2060-2006     440   18    
soft     400-450  45-55   
hard     700-750  7-10   


    Brinell hardness for     LАZH60-1-1   ( ЛАЖ60-1-1 )   ,     soft HB 10 -1 = 45 - 55   MPa
    Brinell hardness for     LАZH60-1-1   ( ЛАЖ60-1-1 )   ,     hard HB 10 -1 = 165 - 175   MPa


Technological properties of the material   LАZH60-1-1   ( ЛАЖ60-1-1 ) .
        Melting temperature : 904   °C
        Forging temperature : 600 - 800   °C
        Annealing temperature : 600 - 650   °C


Physical properties for grade   LАZH60-1-1   ( ЛАЖ60-1-1 )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 1.05   75.3 8300   90
100   21.6        


Equivalent steels for grade     LАZH60-1-1   ( ЛАЖ60-1-1 )
Warning! Indicated both exact and nearest equivalents.
Japan
JIS
C6782



Types of delivery of grade   LАZH60-1-1   ( ЛАЖ60-1-1 )
B55 - Bars


Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]

  LАZH60-1-1   ( ЛАЖ60-1-1 ) - Copper-zinc alloys pressure treated: chemical composition, mechanical and physical properties, hardness
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 3000 steels and alloys